1) charcoal made out of the rod is a density, if the rod is broken on the broken, and in the broken side with a luster: it shows that because the spiral front is too high; (2) in the process of making the bar The temperature is slightly higher on the emergence of carbonization, but the temperature is slightly lower if not a good stick: then charcoal machine sleeve wear is very serious;
(3) the same raw materials in different charcoal machine equipment on the use of even a world of difference: cause this cause is the screw and sleeve with the gap is not appropriate; (4) in the rod when the smoke from the bar around, And the system out of the bar is relatively rough or not a good stick: it is because the rod used raw materials too dry, screw and sleeve with the gap is too large or too high temperature; (5) in the rod often appear blasting, (6) the temperature is too low, the raw material is too wet or with the gap is not suitable, is caused by the lack of wear and tear, the use of this phenomenon is due to the phenomenon of serious wear and tear, the main reason is not smooth rods and shooting; and (7) if the raw material is not large rods humidity drying, the rod will bend out of the system; (8) adjust the screw is too long or the temperature too high will cause the difference in density rods and fast; (9) the same starting material after changing the screw rod slow: the screw spiral first track is too high; (10) the price of the raw material is too wet charcoal or other reasons when the machine does not take a long time operation will stick return air phenomenon occurs; (11) a screw is too Or worn and will cause the screw rod not idle; (12) and a screw threaded rod not live: temperature is too low, or too short spiral wear.